가토의 대퇴부에 Calcium Metaphosphate로 코팅된 임플란트 매식후 골유착에 관한 비교 연구 (Comparative Study on Osseointegration of Calcium Metaphosphate (CMP) Coated Implant to RBM Implant in the Femur of Rabbits)

Purpose: This study was conducted in order to compare the efficacy of osseointegration of three different calcium metaphosphate(CMP) coated implants in the rabbit’s femur.
Materials and Methods: Twenty four rabbits and three different type of CMP coated implants and RBM implants were used in this study. The animals were divided into 4 groups on the basis of implant surface characteristics. Two implants were installed into the condyle of femur of each rabbits. The animals were sacrificed at 2 and 4 weeks after installation. The undecalcified specimens were prepared for histological, radiological examination and histomorphometric analysis of implant-bone contact ratios(BIC) and bone area ratio(BA).
Results: Two implants were failed to osseointegrate and implant success rate was 95.2%. There were not any significant inflammatory response in all groups. Fluorescent image at 4 weeks shows that remodeling is slower in RBM group than CMP group. CMPIII showed more active remodeling than CMPI, II. In histomorphologic analysis, BIC ratio at 2 weeks was lower than 4 weeks.


Conclusion: The results suggest that the ratios of CMP coated implants were higher than that of RBM control group but there is no significantly difference between RBM group and CMP group. In conclusion, CMP coated implant had more clinical availability than RBM implants.

Purpose: This study was conducted in order to compare the efficacy of osseointegration of three different calcium metaphosphate(CMP) coated implants in the rabbit’s femur.
Materials and Methods: Twenty four rabbits and three different type of CMP coated implants and RBM implants were used in this study. The animals were divided into 4 groups on the basis of implant surface characteristics. Two implants were installed into the condyle of femur of each rabbits. The animals were sacrificed at 2 and 4 weeks after installation. The undecalcified specimens were prepared for histological, radiological examination and histomorphometric analysis of implant-bone contact ratios(BIC) and bone area ratio(BA).
Results: Two implants were failed to osseointegrate and implant success rate was 95.2%. There were not any significant inflammatory response in all groups. Fluorescent image at 4 weeks shows that remodeling is slower in RBM group than CMP group. CMPIII showed more active remodeling than CMPI, II. In histomorphologic analysis, BIC ratio at 2 weeks was lower than 4 weeks.


Conclusion: The results suggest that the ratios of CMP coated implants were higher than that of RBM control group but there is no significantly difference between RBM group and CMP group. In conclusion, CMP coated implant had more clinical availability than RBM implants.